Semiconductor integrated circuit device and a method of manufacturing the same

ABSTRACT

This invention is for improving filling properties between vertical MISFETs constituting a SRAM memory cell. Upon formation of vertical MISFETs over horizontal drive MISFETs and transfer MISFETs, they are disposed with a narrow pitch in the Y direction and a wide pitch in the X direction. After a first insulating film (O 3 -TEOS) having good coverage is disposed over a columnar laminates having a lower semiconductor layer, an intermediate semiconductor layer, an upper semiconductor layer and a silicon nitride film and a gate electrode formed over the side walls of the laminates via a gate insulating film to completely fill a narrow pitch space, a second insulating film (HDP silicon oxide film) is deposited over the first insulating film, resulting in an improvement in the filling properties even in a narrow pitch portion between the vertical MISFETs having a high aspect ratio.

TECHNICAL FIELD

[0001] The present invention relates to a semiconductor integrated circuit device and a manufacturing technique thereof, particularly to a technique effective when applied to a semiconductor integrated circuit device having a vertical MISFET.

BACKGROUND OF THE INVENTION

[0002] Semiconductor integrated circuit devices have many layer-stack structures each having a conductive film and an insulating film. This insulating film tends to be formed in order to insulate between conductive films. For example, plural interconnect layers are separated by an insulating film. An element formation region of a semiconductor substrate is also separated by an insulating film filled in a groove.

[0003] The space between interconnects or a groove space however tends to be narrower with a recent tendency toward high integration and miniaturization of the device. In some parts, a ratio of the width to the height of a space (aspect ratio=height/width) becomes large.

[0004] Various improvements have been made to fill such a space accurately.

[0005] For example, in Patent Document 1, disclosed is a technique of filling a first insulating film (46) in a region having a fine line width and a high height/width ratio, for example, a space between conductive lines (42), carrying out dry etch back (50) to remove voids (48) and then forming a second insulating film (52) over the first insulating film.

[0006] Patent Document 1: Japanese Patent Laid-Open No. Hei 11(1999)-176936

SUMMARY OF THE INVENTION

[0007] The present inventors have been engaged in researches and development of semiconductor integrated circuit devices. They have carried out an investigation particularly on the structure or manufacturing method of SRAM (Static Random Access Memory) which is a kind of a semiconductor memory device.

[0008] With regards to the SRAM investigated by the present inventors, its memory cell is formed of, for example, four n-channel type MISFETs (Metal-Insulator-Semiconductor-Field-Effect-Transistor) and two p channel type MISFETS.

[0009] Since a reduction in the memory size cannot be attained easily when these six MISFETs constituting the memory cell of SRAM are disposed on the same plane, formation of two vertical p channel type MISFETs over the four horizontal type MISFETs which will be described later are under investigation.

[0010] It has been revealed that when vertical type MISFETs are employed, it becomes difficult to fill an insulating film between them.

[0011] Described specifically, a vertical type MISFET is made of a columnar semiconductor having source and drain regions thereover and therebelow, respectively. A ratio (aspect ratio) of the height of this columnar semiconductor to the space between two adjacent columnar semiconductors is much greater than the aspect ratio of the space between interconnects or that of an element isolation groove which have been studied conventionally. It is therefore necessary to study a technique capable of filling a space between columnar semiconductors with good accuracy.

[0012] In particular, when a distance between two columnar semiconductors in the X direction is different from that in the Y direction in consideration of the layout of underlying horizontal MISFETs and vertical MISFETs, it is necessary to fill, with good accuracy, the space whether it is narrow or wide.

[0013] An object of the present invention is to provide a technique capable of improving filling properties in a space between vertical MISFETs constituting a semiconductor integrated circuit device.

[0014] Another object of the present invention is to improve the properties of a semiconductor integrated circuit device having vertical MISFETs, and also to attain miniaturization of the device.

[0015] The above-described and the other objects and novel features of the present invention will be apparent from the description herein and accompanying drawings.

[0016] The outline of the typical inventions, of the inventions disclosed by the present application, will next be described.

[0017] In one aspect of the present invention, there is thus provided a semiconductor integrated circuit device comprising a plurality of vertical MISFETs having (a1) a columnar laminate having, at the upper portion and lower portion thereof, a first and second semiconductor regions, respectively and (a2) a conductive film formed over side walls of the columnar laminate via a first insulating film, wherein the plurality of vertical MISFETs having the columnar laminate and the conductive film are (b1) spaced by a first distance in a first direction, and (b2) spaced by a second distance greater than the first distance in a second direction; and up to at least a predetermined height of the columnar laminate of each of the plurality of vertical MISFETs, (c1) a second insulating film is formed in the space of the columnar laminates in the first direction and (c2) the second insulating film and a third insulating film thereover are formed in the space of the columnar laminates in the second direction.

[0018] In a second aspect of the present invention, there is also provided a manufacturing method of a semiconductor integrated circuit device, comprising (a) forming a plurality of columnar laminates having, at the upper portion and lower portion thereof, first and second semiconductor regions, respectively while spacing the columnar laminates in a first direction and in a second direction with a space in the second direction being wider than that in the first direction, (b) forming a conductive film over the side walls of each of the columnar laminates via a first insulating film and setting a distance, in the first direction, between the conductive films over the side walls of the columnar laminates as a first distance and a distance in the second direction as a second distance greater than the first distance, (c) forming a second insulating film to be thick enough to fill the first distance but not the second distance, and (d) forming a third insulating film over the second insulating film, while filling the second distance.

[0019] In a third aspect of the present invention, there is also provided a manufacturing method of a semiconductor integrated circuit device, which comprises (a) forming a semiconductor film having, at the upper portion and lower portion thereof, first and second semiconductor regions, respectively, (b) etching the semiconductor film with a mask which is H-shaped in the X direction, thereby forming an approximately elliptical columnar laminate having a longer diameter in a second direction perpendicular to the first direction, and (c) forming a conductive film over the side walls of the columnar laminate via an insulating film.

[0020] In a fourth aspect of the present invention, there is also provided a semiconductor integrated circuit device comprising (a) a columnar laminate having, at the upper and lower portions thereof, first and second semiconductor regions, respectively and having a substantially elliptical columnar plane pattern; and (b) a conductive film formed over the side walls of the columnar laminate via an insulating film.

BRIEF DESCRIPTION OF THE DRAWINGS

[0021]FIG. 1 is an equivalent circuit diagram of a SRAM memory cell according to one embodiment of the present invention;

[0022]FIG. 2 is a fragmentary cross-sectional view of a substrate illustrating a manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0023]FIG. 3 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0024]FIG. 4 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0025]FIG. 5 is fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0026]FIG. 6 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0027]FIG. 7 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0028]FIG. 8 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0029]FIG. 9 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0030]FIG. 10 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0031]FIG. 11 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0032]FIG. 12 is a plan view illustrating a transfer pattern (reticle pattern) to be used for a manufacturing step of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0033] FIGS. 13(a) and 13(b) show a table illustrating the relationship between the transfer pattern and etched shape (plane pattern of laminate);

[0034]FIG. 14 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0035]FIG. 15 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0036]FIG. 16 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0037]FIG. 17 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0038]FIG. 18 is a fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0039]FIG. 19 is a fragmentary perspective view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0040]FIG. 20 is a fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0041]FIG. 21 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0042]FIG. 22 is a fragmentary perspective view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0043]FIG. 23 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0044]FIG. 24 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0045]FIG. 25 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0046]FIG. 26 is a fragmentary perspective view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0047]FIG. 27 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0048]FIG. 28 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0049]FIG. 29 is fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0050]FIG. 30 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0051]FIG. 31 is fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0052]FIG. 32 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0053]FIG. 33 is fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0054]FIG. 34 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0055]FIG. 35 is a fragmentary plan view of a substrate of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0056]FIG. 36 is a fragmentary layout diagram of a substrate of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0057]FIG. 37 is a fragmentary plan view of a substrate of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0058]FIG. 38 is fragmentary plan view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0059]FIG. 39 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0060]FIG. 40 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) for describing the advantages of the one embodiment of the present invention;

[0061]FIG. 41 is fragmentary cross-sectional view of a substrate illustrating the manufacturing method of the semiconductor integrated circuit device (SRAM) for describing the advantages of the one embodiment of the present invention;

[0062]FIG. 42 is an equivalent circuit diagram of another SRAM memory cell according to the one embodiment of the present invention;

[0063]FIG. 43 is a fragmentary plan view of a substrate illustrating the another semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0064]FIG. 44 is a fragmentary cross-sectional view of a substrate illustrating the another semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention;

[0065]FIG. 45 is a fragmentary plan view of a substrate illustrating the another semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention; and

[0066]FIG. 46 is a fragmentary cross-sectional view of a substrate illustrating a further semiconductor integrated circuit device (SRAM) according to the one embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0067] The embodiments of the present invention will hereinafter be described specifically based on accompanying drawings. In all the drawings for describing the below-described embodiments, members having like function will be identified by like reference numerals and overlapping descriptions will be omitted. To facilitate understanding of the description, some parts (for example, an insulating film) are described while attaching thereto an ordinal number “first”, “second” or the like, but this does not always corresponds to “first”, “second” or the like in claims.

[0068]FIG. 1 is an equivalent circuit diagram of a memory cell of a SRAM according to the embodiment of the present invention. As illustrated in FIG. 1, this memory cell (MC) of a SRAM are each constituted of two horizontal transfer MISFETs (TR1 and TR2, each of which will hereinafter be called “transfer MISFET” simply), two horizontal drive MISFETs (DR1 and DR2, each of which will hereinafter be called “drive MISFET” simply), and two vertical load MISFETs (SV1 and SV2, each of which will hereinafter be called “vertical MISFET” simply), each disposed at the intersection of a pair of complementary data lines (BLT and BLB) and a word line (WL).

[0069] Of the six MISFETs constituting the memory cell (MC), two transfer MISFETs (TR1 and TR2) and two drive MISFETs (DR1 and DR2) are each made of an n channel type MISFET. The two vertical MISFETs (SV1 and SV2) are each made of a p channel type MISFET.

[0070] As described later, the vertical MISFETs (SV1 and SV2) are disposed over formation regions of the drive MISFETs (DR1 and DR2) and transfer MISFETs (TR1 and TR2).

[0071] As illustrated in FIG. 1, the drive MISFET (DR1) and vertical MISFET (SV1) of the memory cell (MC) constitute a first inverter INV₁, while the drive MISFET (DR2) and vertical MISFET (SV2) constitute a second inverter INV₂. The input and output portions for the pair of the inverters INV₁ and INV₂ are crosslinked within the memory cell (MC) and constitute a flip flop circuit as an information storing unit for storing information of 1 bit.

[0072] Described specifically, two pairs of MISFETs constituting the inverter are connected in series between a reference voltage (Vss) and a supply voltage (Vdd, for example, 3V) and the connecting nodes (output portions, A and B) of them are cross-connected to the connecting portions (input portions) of these gate electrodes.

[0073] In other words, the drain (one end) of the drive MISFET (DR1), the drain of the vertical MISFET (SV1), the gate of the drive MISFET (DR2) and the gate of the vertical MISFET (SV2) are electrically connected each other. Each portion of these MISFETs is connected to one storage node (A) of the memory cell. The drain of the drive MISFET (DR2), the drain of the vertical MISFET (SV2), the gate of the drive MISFET (DR1) and the gate of the vertical MISFET (SV1) are electrically connected each other. Each portion of these MISFETs is connected to one storage node (B) of the memory cell.

[0074] Between the storage nodes (A and B) and the complementary data lines (BLT and BLB), the transfer MISFETs (TR1 and TR2) are electrically connected, respectively. The gate electrodes of the transfer MISFETS (TR1 and TR2) are electrically connected to the word line (WL).

[0075] The above-described memory cell (MC) stores data by setting the potential of one of the paired storage nodes (A and B) high (High) and that of the other one low (Low).

[0076] Upon reading of the data of the memory cell (MC), a supply voltage (Vdd) is applied to a selected word line (WL) to turn the transfer MISFETS (TR1 and TR2) ON and a potential difference between the paired storage nodes (A and B) is read via the complementary data lines (paired data lines, BLT and BLB).

[0077] Upon writing, a supply voltage (Vdd) is applied to a selected word line (WL) to turn the transfer MISFETS (TR1 and TR2) ON and at the same time, one of the complementary data lines (BLT and BLB) is connected to the supply voltage (Vdd), while the other is connected to the reference voltage (Vss), whereby the ON and OFF of the drive MISFETs (DR1 and DR2) are inverted.

[0078] FIGS. 2 to 34 (except FIGS. 12 and 13) are a fragmentary cross-sectional view, fragmentary plan view or fragmentary perspective view of a substrate illustrating a manufacturing method of the semiconductor integrated circuit device (SRAM) according to this embodiment. In each cross-sectional view, a diagram on the left side is a view taken along a line A-A′ of the plan view, a diagram at the center is a view taken along a line B-B′ of the plan view and a view on the right side is a view taken along a line C-C′.

[0079] The characteristic structure of the semiconductor integrated circuit device (SRAM) according to this embodiment will next be described. Its detailed structure will be described in accordance with the manufacturing steps.

[0080] As illustrated in FIGS. 33 and 34 which are final step views, the SRAM memory cell is formed in a substantially rectangular cell region surrounded by the mark (+) in the diagram; the drive MISFETs (DR1 and DR2) and transfer MISFETs which are horizontal transistors are formed in a relatively lower-layer region; and the vertical MISFETs (SV1 and SV2) are formed in a region upper than the above-described four regions.

[0081] What is characteristic in the SRAM of this embodiment is that a space between SV1 and SV2 of the vertical MISFET in the Y direction (a direction of B-B′) is, as illustrated in the center diagram of FIG. 34, filled with a single layer of a first insulating film (O₃-TEOS film) 70 a up to the vicinity of the upper portion of its gate electrode 66, while a space in the X direction has a stacked structure of a first insulating film (O₃-TEOS film) 70 a and a second insulating film (HDP oxide film) 70 b.

[0082] As illustrated in FIG. 35, cell regions are disposed in the array form in the X and Y directions and each cell region is disposed axisymmetric to a short side of the cell region running in the Y direction and axisymmetric to a long side of the cell region running in the X direction. Each pattern in the cell region is disposed point-symmetric to the central point of the cell region.

[0083] The vertical MISFETs (SV1 and SV2) are therefore disposed in the array form in the X and Y directions. They are spaced by a distance D1 in the Y direction and with a distance D2 (D2>D1) in the X direction. In FIG. 35, some of the patterns (SV1, SV2, 42, 43 and the like) shown in FIG. 33 are shown.

[0084] With regards to the positional relationship between the vertical MISFETs (columnar laminates (P1 and P2) and gate electrode 66) disposed in the array form and the first insulating film 70 a, the columnar laminates (P1 and P2) and the gate electrodes 66 arranged in the Y direction seem to be embedded in a projecting portion 172 a extending in the Y direction of the first insulating film (O₃-TEOS film) 70 a (refer to FIG. 26).

[0085] Between the projecting portions extending in the direction Y of the first insulating film (O₃-TEOS film) 70 a, a second insulating film (HDP oxide film) 70 b is filled (refer to FIG. 26). The columnar laminates (P1 and P2) protruded from the first insulating film (O₃-TEOS film) 70 a are covered with a fourth insulating film (P-TEOS film) 73 (refer to FIG. 34).

[0086] The plane pattern of each of the columnar laminates (P1 and P2) disposed in the array form can be formed, as illustrated in FIG. 17, as approximately elliptic. The longer diameter of this approximately elliptic pattern is located in a long-side direction (X direction) of the cell region.

[0087] By forming the approximately elliptical pattern of the columnar laminates (P1 and P2) to be longer in the direction where they are spaced widely (with a wide pitch), a channel region can be widened and a channel current can be increased. In addition, a size reduction in the cell region can be attained.

[0088] A specific structure of the semiconductor integrated circuit device (SRAM) according to this embodiment will next be described in detail in the order of manufacturing steps.

[0089] As illustrated in FIGS. 2 and 3, an element isolation is formed in a substrate 1 made of, for example, p type single crystal silicon. This element isolation is formed by, for example, making a groove 2 in the substrate 1, thermally oxidizing the resulting substrate, and then filling a silicon oxide film 3 in the groove as an insulating film. An exposed region of the substrate 1 surrounded by this element isolation will be an element formation region (active region) L.

[0090] Into a part of the substrate 1, a p type impurity (for example, boron (B) is ion-implanted and thermally diffused, whereby a p type well 4 is formed over the main surface of the substrate 1.

[0091] A region shown in FIGS. 2 and 3 is a memory region, around which a peripheral circuit region exists, though not illustrated. In addition to the p type well, an n type well is formed in this peripheral circuit region by diffusion of an n type impurity. Over the main surface of the p type well, an n channel type MISFETQn is formed in similar steps to those employed for the formation of a horizontal MISFET which will be described later, and a p channel type MISFETQp is formed by a step using an impurity having an opposite conductivity type (refer to FIG. 39). These MISFETs constitute various circuits for driving a memory, for example, X decoder (Xdec) or Y decoder (Ydec) as illustrated in FIG. 36. In FIG. 36, PA represents a peripheral circuit region, while MA represents a memory region.

[0092] Over the surface of the p type well 4, a gate insulating film 6 having a thickness of about from 3 nm to 4 nm is formed. This gate insulating film 6 is made of, for example, a silicon oxide film and it is formed by thermal oxidation of the substrate 1.

[0093] Over the gate insulating film 6, a polycrystalline silicon film having, for example, an n type impurity doped therein is deposited as a conductive film, followed by deposition thereover of a silicon oxide film as a cap insulating film by, for example, chemical vapor deposition (CVD).

[0094] The above-described silicon oxide film is then patterned, and with this patterned silicon oxide film as a mask, the n type polycrystalline silicon film is dry etched to form gate electrodes 7A,7B over the p type well 4. Compared with a photoresist film, silicon oxide has a greater etching selectivity to polycrystalline silicon so that by using silicon oxide as a mask, patterning of a minute gate electrode can be attained with good accuracy. The gate electrode 7A constitutes a gate electrode of the transfer MISFETs (TR1 and TR2), while the gate electrode 7B constitutes the gate electrode of the drive MISFETs (DR1 and DR2). As illustrated in FIG. 3, the gate electrodes 7A,7B have a rectangular plane pattern extending in the direction X and their width in the direction Y, that is, gate length is, for example, from 0.13 to 0.14 μm.

[0095] By ion implantation of an n type impurity (for example, phosphorous or arsenic) into the p type wells 4 on both sides of the gate electrodes 7A,7B, an n⁻ type semiconductor regions 9 having a relatively low concentration is formed.

[0096] After successive deposition, over the substrate 1, of a silicon oxide film and a silicon nitride film as insulating films by CVD, these films are anisotropically etched to form side wall spacers 13 on the side walls of the gate electrodes 7A,7B. By this anisotropic etching, the silicon oxide film over the gate electrodes and the gate insulating film (silicon oxide film) 6 over the surface of the substrate 1 are removed.

[0097] By ion implantation of an n type impurity (for example, phosphorous or arsenic) into the p type wells 4 on both sides of the gate electrodes 7A,7B, n⁺ type semiconductor regions 14 having a relatively high concentration are formed.

[0098] By the steps so far mentioned, the transfer MISFETs (TR1 and TR2) and drive MISFETs (DR1 and DR2) having source and drain regions of an LDD structure are formed. Of these four MISFETs, TR1 and DR1 have one of the source and drain regions in common and TR2 and DR2 have one of the source and drain regions in common.

[0099] Over the substrate 1, a cobalt (Co) film is then deposited as a high melting point metal film by, for example, sputtering, followed by heat treatment, whereby a silicide reaction is caused on the interface between the Co film and the gate electrodes 7A,7B and the Co film and the substrate 1 (n⁺ type semiconductor region 14), and a silicide layer 18 is formed. Then, an unreacted portion of the Co film is removed by etching.

[0100] Over the MISFETs (TR1, TR2, DR1 and DR2), a silicon nitride film 19 and a silicon oxide film 20 are deposited as an insulating film by, for example, CVD and then, the surface of the silicon oxide film 20 is planarized by chemical mechanical polishing (CMP).

[0101] With a photoresist film as a mask, the silicon oxide film 20 and silicon nitride film 19 are dry etched to form a contact hole 21 over the gate electrode 7A of the transfer MISFETs (TR1 and TR2) and a contact hole 22 over the gate electrode 7B of the drive MISFETs (DR1 and DR2). In addition, contact holes 23,24,25 are formed over the source and drain (n⁺ type semiconductor regions 14) of each of the transfer MISFETs (TR1, TR2) and drive MISFETs (DR1, DR2). Of these, the contact hole 23 is formed over the source and drain regions which are common to TR1 and DR1, and TR2 and DR2.

[0102] Over the silicon oxide film 20 including the insides of the contact holes 21 to 25, a laminate of a titanium (Ti) film and a titanium nitride (TiN) film are deposited as a barrier film by, for example, sputtering. After deposition of a tungsten (W) film as a conductive film by, for example, CVD, the W film outside the contact holes 21 to 25 are removed by CMP, whereby a plug 28 is formed inside of the contact holes 21 to 25.

[0103] As illustrated in FIGS. 4 and 5, a silicon nitride film 29 and a silicon oxide film 30 are successively deposited as an insulating film over the substrate 1 by, for example, CVD, followed by dry etching of these films, whereby grooves 31 to 35 are formed over the contact holes 21 to 25, respectively. Of these, the grooves 32 and 33 each extends from the upper part of the contact hole 22 toward the upper part of the contact hole 23. The silicon nitride film 29 serves as a stopper film upon etching of the silicon oxide film 30.

[0104] Over the silicon oxide film 30 including the insides of the grooves 31 to 35, a TiN film is deposited as a barrier film by, for example, sputtering, followed by deposition of a W film as a conductive film by, for example, CVD. The W film outside the grooves 31 to 35 is then removed by CMP to form intermediate conductive layers 41 to 45. FIG. 6 illustrates a fragmentary plan view of a memory cell array after the formation of the intermediate conductive layer. As described above, cell regions are disposed in the array form in the X and Y directions and each cell region is disposed axisymmetric to a short side of the cell region running in the Y direction and axisymmetric to a long side of the cell region running in the X direction. Each pattern in the cell region is disposed point-symmetric to the central point of the cell region.

[0105] Of the intermediate conductive layers 41 to 45 shown in FIG. 5, a pair of the intermediate conductive layers 42,43 formed at almost the center of the memory cell region correspond to the storage nodes A,B of FIG. 1.

[0106] Described specifically, the intermediate conductive layer 42(A) is electrically connected to the source and drain regions (n⁺ type semiconductor regions 14) common to TR1 and DR1 and the gate electrode 7B of DR2, while the intermediate conductive layer 43(B) is electrically connected to the source and drain regions (n⁺ type semiconductor regions 14) common to TR2 and DR2 and the gate electrode 7B of DR1.

[0107] Over the intermediate conductive layers 42(A) and 43(B), vertical MISFETs (SV1) and (SV2) are then formed, respectively. The gate electrode of SV1 is connected to the intermediate conductive layer 43(B) and the gate electrode of SV2 is connected to the intermediate conductive layer 42(A).

[0108] In addition, a word line (WL) is formed over the intermediate conductive layer 41, bit lines (BLT, BLB) are formed over the intermediate conductive layer 44, and a reference voltage (Vss) line is formed over the intermediate conductive layer 45. Over the vertical MISFET, a supply voltage line (Vdd) is formed.

[0109] Manufacturing steps of the vertical MISFET and various interconnects will next be described.

[0110] In the fragmentary plan views of FIGS. 7 to 32, in order to facilitate the understanding of them, patterns of layers below the intermediate conductive layer are omitted.

[0111] As illustrated in FIGS. 7 and 8, for example, a WN film is deposited over the surfaces of the intermediate conductive layers 42,43 by sputtering, followed by patterning, whereby a barrier layer 48 is formed. This barrier layer 48 is formed to prevent occurrence of undesired silicide reaction on the interface between a silicon film constituting a plug 55 and the intermediate conductive layers 42,43. It may therefore be formed only over the formation region of the plug 55.

[0112] After deposition of a silicon nitride film 49 as an insulating film over the substrate 1 by, for example, CVD, a polycrystalline silicon film (or amorphous silicon film) having a p type impurity doped therein is deposited as a conductive film by, for example, CVD over the silicon nitride film.

[0113] By patterning the polycrystalline silicon film, a pair of gate extraction electrodes 51 (51 a,51 b) are formed. The gate extraction electrodes 51 are disposed in a region adjacent to the plane patterns of the vertical MISFETs (SV1,SV2) which will be formed later and they are connected to the gate electrode (66) of the vertical MISFETs (SV1,SV2). The gate extraction electrodes 51 a,51 b are disposed in the vicinity of the intermediate conductive layers 42,43, respectively.

[0114] Formation of the plug 55 to be connected to the vertical MISFET and the gate extraction electrodes 51 a,51 b at the above-described positions in almost the same layer enables to connect the gate extraction electrode to the gate electrode in self alignment and moreover, to reduce a vertical difference between the gate extraction electrode and intermediate conductive layers 42,43, making it possible to connect them via a tungsten (W) plug 80 which will be described later.

[0115] As illustrated in FIG. 9, a silicon oxide film 52 is deposited as an insulating film over the silicon nitride film 49 by, for example, CVD to cover the gate extraction electrode 51. The silicon oxide film 52 over the barrier layer 48 is then dry etched to form a through-hole 53. The silicon nitride film 49 functions as a stopper film upon etching of the silicon oxide film 52.

[0116] A silicon oxide film is deposited by CVD over the silicon oxide film 52 including the inside of the through-hole 53, followed by anisotropic etching of the silicon oxide film to form, over the side walls of the through-hole 53, side wall spacers 54 made of an insulating film. By this anisotropic etching, the silicon nitride film 49 at the bottom of the through-hole 53 is also etched.

[0117] After deposition, over the silicon oxide film 52 including the inside of the through-hole 53, of a polycrystalline silicon film (or amorphous silicon film) having a p type impurity doped therein, by, for example, CVD, the polycrystalline silicon film outside the through-hole 53 is removed by CMP (or etch back) to form the plug 55 inside of the through-hole 53.

[0118] Over the silicon oxide film 52 including the upper part of the plug 55, a p type silicon film 57 p, a silicon film 58 i and a p type silicon film 59 p are formed. These three layers of silicon films (57 p, 58 i, 59 p) are formed, for example, in the following manner. After successive deposition of an amorphous silicon film having boron doped therein and a non-doped amorphous silicon film by CVD, these amorphous silicon films are heat treated to crystallize the same. After ion implantation, into the silicon film 58 i, of an n type or p type impurity for the channel formation, an amorphous silicon film having boron doped therein is deposited over the-silicon film 58 i by CVD, followed by crystallization of the resulting amorphous silicon film by heat treatment. Over the p type silicon film 59 p, a thin silicon oxide film 61 and a silicon nitride film 62 are deposited over the p type silicon film 59 p successively as a cap insulating film by, for example, CVD.

[0119] As illustrated in FIGS. 10 and 11, with an unillustrated photoresist film as a mask, the silicon nitride film 62 is dry etched to leave the silicon nitride film 62 over a region in which the vertical MISFETs (SV1, SV2) are to be formed. With the silicon nitride film 62 as a mask, the three silicon films (57 p, 58 i, 59 p) are dry etched, whereby columnar laminates (P1, P2) having a lower semiconductor layer (semiconductor region) 57 made of the p type silicon film 57 p, an intermediate semiconductor layer 58 made of the silicon film 58 i and an upper semiconductor layer 59 made of the p type silicon film 59 p are formed. At this time, the silicon nitride film 62 still remains over the upper semiconductor layer 59.

[0120] The lower semiconductor layer 57 of the laminate (P1) constitutes the drain of the vertical MISFET (SV1), while the upper semiconductor layer 59 constitutes the source of it. The intermediate semiconductor layer 58 existing between the lower semiconductor layer 57 and the upper semiconductor layer 59 substantially constitutes the substrate of the vertical MISFET (SV1) and its side walls constitute the channel regions. The lower semiconductor layer 57 of the laminate (P2) constitutes the drain of the vertical MISFET (SV2) and the upper semiconductor layer 59 constitutes the source of it. The intermediate semiconductor layer 58 substantially constitutes the substrate of the vertical MISFET (SV2) and its side walls constitute the channel regions.

[0121] In this Embodiment, a transfer pattern (reticle pattern) upon patterning of a photoresist film used for etching of the silicon nitride film 62 is formed to have a shape as illustrated in FIG. 12. As illustrated in FIG. 12, this transfer pattern (which may be called “transfer mask”) is H-shaped when viewed from the Y direction. As described later based on FIGS. 13(a) and 13(b), this transfer pattern (transfer mask) is H-shaped, more specifically, it does not have a uniform width in the Y direction and is narrower at the center thereof than the both ends. In FIG. 12, the patterns of the intermediate conductive layers 42,43 are also shown in order to facilitate the understanding of the positional relationship between the pattern of an actual device and the transfer pattern.

[0122] According to this embodiment, use of a transfer mask which has been H-shaped in the Y direction enables etching of the photoresist film into an approximately elliptical etching pattern having a longer diameter in the X direction. By etching of the silicon nitride film 62 through this approximately elliptical etching pattern and then, etching of the columnar laminates (P1, P2) through the resulting silicon nitride film 62 thus etched into an approximate ellipse, it is possible to make the plane pattern of the columnar laminates (P1, P2) into an approximately elliptical shape longer in the X direction (refer to FIG. 17). Since the transfer mask which has been H-shaped in the Y direction is used, an approximately elliptical etching pattern having a longer diameter in the X direction can be formed and the columnar laminates (P1,P2) can be formed to have an approximately elliptical shape longer in the X direction.

[0123] As a result, the distance between any two adjacent columnar laminates in the Y direction can be narrowed, making it possible to increase the channel region (channel current) of the vertical MISFET while attaining miniaturization of a cell region.

[0124] FIGS. 13(a) and 13(b) show the relationship between the transfer pattern and etched shape (plane pattern of the laminate). As illustrated in FIG. 13(b), the transfer pattern is H-shaped in the Y direction. In other words, a rectangle having a short side (300 nm) and a long side (320 nm) lacks, at both ends at the center of the two long sides (direction X), a rectangular pattern having a predetermined width (120 nm) in the X direction and a predetermined depth (70 nm) in the Y direction. In short, the transfer pattern is H-shaped with its width in the Y direction narrower, at the center of the X direction, than both ends of the pattern.

[0125] When the transfer pattern having the above-described size is used, the plane pattern of the laminate is elliptical with a longer diameter of about 270 nm and a shorter diameter of about 230 nm.

[0126] When a square transfer pattern 240 nm on a side as illustrated in FIG. 13(a) is used, on the other hand, the plane pattern of the laminate does not become a complete circle but approximately circular (longer diameter: 236 nm, shorter diameter: 224 nm).

[0127] In the plain views and perspective views other than FIG. 17, a plane pattern of each of the silicon nitride film 62 and columnar laminates (P1, P2) is illustrated as a rectangular one for convenience sake.

[0128] Upon dry etching of the above-described silicon films (57 p, 58 i, 59 p), a taper may be formed on the bottom of the side walls of the laminates (P1, P2) as illustrated in FIG. 10. An increase in the contact resistance between the lower semiconductor layer 57 and the plug 55 due to misalignment can be suppressed by the formation of a taper.

[0129] Upon forming the laminates (P1, P2), a thin (several nm or less) tunnel insulating film composed of a silicon nitride film or the like may be disposed in the vicinity of the interface between the upper semiconductor layer 59 and the intermediate semiconductor layer 58, in the vicinity of the interface between the lower semiconductor layer 57 and the intermediate semiconductor layer 58, or at the center of the intermediate semiconductor layer 58. Provision of this tunnel insulating film enables to prevent diffusion of an impurity in the lower semiconductor layer 57 or in the upper semiconductor layer 59 to the inside of the intermediate semiconductor layer 58.

[0130] As illustrated in FIGS. 14 and 15, a gate insulating film 63 is formed over the surface of the side walls of the lower semiconductor layer 57, intermediate semiconductor layer 58 and upper semiconductor layer 59 which layers constitute each of the laminates (P1, P2). This gate insulating film 63 is made of, for example, a silicon oxide film and is formed by subjecting the substrate 1 to low-temperature thermal oxidation (for example, wet oxidation) at 800° C. or less. Since the silicon oxide film 61 has been formed between the laminates (P1, P2) and the silicon nitride film 62 thereover, contact between the gate insulating film 63 formed on the surface of the upper semiconductor layer 59 with the silicon nitride film 62 can be prevented, and therefore, lowering in the withstand pressure of the gate insulating film 63 in the vicinity of the upper end portion of the laminates (P1, P2) can be prevented. The gate insulating film may be formed of a deposited film.

[0131] After a first polycrystalline silicon film 64 having a p type impurity doped therein is deposited, as a conductive film, over the silicon oxide film 52 and columnar laminates (P1, P2) by using, for example, CVD, this polycrystalline silicon film is anisotropically etched to leave the first polycrystalline silicon film so as to surround therewith the side walls of the columnar laminates (P1, P2) and silicon nitride film 62. By forming the first polycrystalline silicon film 64, which partially constitutes the gate electrode (66), as described above in self alignment, the memory size can be reduced. Upon etching of this polycrystalline silicon film 64, the silicon oxide film 52 lying therebelow is etched successively.

[0132] As illustrated in FIGS. 15 and 16, a second polycrystalline silicon film 65 having a p type impurity doped therein is formed, as a conductive film, over the surfaces of the silicon nitride film 49 and first polycrystalline silicon film 64 by, for example, CVD. By anisotropic etching of this polycrystalline silicon film, the second polycrystalline silicon film 65 is left so as to surround therewith the surface of the first polycrystalline silicon film 64.

[0133] The second polycrystalline silicon film 65 is also formed over the surfaces of the gate extraction electrodes 51 (51 a, 51 b) and it is electrically connected to the gate extraction electrodes 51. The second polycrystalline silicon film 65 is also formed in self alignment so that the memory size can be reduced.

[0134] By the steps so far mentioned, the gate electrode 66 of the vertical MISFETs (SV1, SV2) made of a laminate of the first polycrystalline silicon film 64 and the second polycrystalline silicon film 65 is formed so as to cover the columnar laminates (P1, P2) and the silicon nitride film 62.

[0135]FIG. 17 is a fragmentary plan view illustrating the relationship between the columnar laminate and gate electrode in the memory cell array (plural cell regions). FIG. 18 is a schematic fragmentary cross-sectional view of the vertical MISFET after formation of the gate electrode 66, in which the left diagram is a view taken along a line X-X′ of FIG. 16, while the right diagram is a view taken along a line Y-Y′ of FIG. 16. In cross-sectional views of FIGS. 18 to 27, layers below the plug 55 are omitted. Some films such as gate insulating film 63 are also omitted. The gate extraction electrodes 51 (51 a, 51 b) are formed at a position lower than the lower semiconductor layer 57, but in these diagrams, they are illustrated adjacent to the lower semiconductor layer 57. FIG. 19 is a fragmentary perspective view illustrating the state of the gate electrode 66 covering the side walls of the columnar laminate in the memory cell array (in the perspective view, the gate extraction electrode is omitted. This will equally apply to FIGS. 22 and 26).

[0136] As illustrated in FIG. 17, patterns each made of the columnar laminate (P1 or P2) and gate electrode 66 are disposed in the array form in the X and Y directions. They are spaced by, for example, 1000 to 1200 nm (for example, about 1040 nm) in the X direction, while the spacing (pitch) in the Y direction is 60 nm. With regards to the arrangement of the columnar laminate and gate electrode, there exist, for example, narrow pitch portions (D1) of 150 nm or less and wide pitch portions (D2) of 500 nm or greater.

[0137] Supposing that the lower semiconductor layer 57, intermediate semiconductor layer 58, upper semiconductor layer 59 and silicon nitride layer 62 constituting the columnar laminate are 300 nm, 300 nm, 300 nm and 300 nm thick, respectively, the height of the columnar laminate becomes about 1200 nm. The aspect ratio of the narrow pitch portion is about 20. When the aspect ratio of the narrow pitch portion exceeds 3, it becomes difficult to fill an insulating film between the adjacent two columnar patterns (P1, 66) with good accuracy. When the aspect ratio exceeds 6, an insulating film cannot be filled with good accuracy even if a conventional technique for filling in a spacing between interconnects or an isolation groove is employed. The aspect ratio of the wide pitch portion, on the other hand, becomes about 1.

[0138] In the next place, a step of filling an insulating film between a plurality of columnar patterns (P1, 66) having both a narrow pitch portion and a wide pitch portion will next be described.

[0139] As illustrated in FIGS. 20 to 22, a first insulating film 70 a having good coverage is deposited. A so-called TEOS film can be given as an example of a film having good coverage. This TEOS film is a film formed by CVD with tetraethoxysilane (Si(OC₂H₅)₄) as a raw material. Examples include an O₃-TEOS film obtained using an active oxidizing species such as ozone (O₃) as another raw material to heighten the reactivity of the film, and a P-TEOS film whose reaction is conducted under a plasma atmosphere.

[0140] The O₃-TEOS film has better coverage than the p-TEOS film so that it is suited as the first insulating film 70 a.

[0141] Examples of another film having good coverage include thermal CVD films obtained by monosilane or disilane as a raw material and can be made reactive by heat. In this case, however, heat treatment at 700° C. or greater (preferably 800° C.) for about 10 hours is necessary. A deterioration in device properties due to a thermal stress is inevitable. In a manufacturing process of a miniaturized and highly-integrated device such as the SRAM of the present invention, there exists a thermal stress standard of limiting application of a thermal stress to a predetermined time in terms of a standard temperature throughout the manufacturing steps. It is difficult to satisfy this thermal load standard when the thermal CVD film is employed.

[0142] The O₃-TEOS film, on the other hand, can be formed at 700° C. or less so that a film with good coverage is available while reducing a thermal stress in the manufacturing steps.

[0143] The following is one example of the film forming conditions of an O₃-TEOS film. It is formed under conditions of a TEOS flow rate of from 800 to 2000 mgm (milligram per minute), an O₃ flow rate of from 5000 to 10000 sccm, a nitrogen (N₂) flow rate of from 8000 to 20000 sccm, temperature at from 450 to 600° C., and subnormal pressure of 600 Torr (1 Torr=1.33322×10² Pa) while using tetraethoxysilane (TEOS) and O₃ as raw materials. Spacing from a susceptor for loading a wafer thereon and a shower head portion which is a raw material gas feeding part is, for example, from 200 to 400 mils. The pressure may fall within a range of from 20 to 760 Torr.

[0144] The P-TEOS film is formed under the conditions, for example, of 300° C. and atmosphere of about 5 to 10 Torr while using tetraethoxisilane and oxygen as raw materials.

[0145] After formation of the first insulating film (O₃-TEOS film) 70 a, it may be heat treated at, for example, 700° C. for 1 minute in order to densify the film.

[0146] As illustrated in FIG. 21, the first insulating film 70 a is thick enough to fill therewith narrow pitch portions completely but not enough to fill wide pitch portions. Described specifically, after formation of the first insulating film 70 a, a concave portion 170 is formed over a wide-pitch space. The thickness of the first insulating film 70 a is adjusted to the narrow-pitch space (D1=60 nm) or greater in consideration of the variations in the size between the pitches or the margin of the film thickness. The upper space between the two adjacent columnar patterns (P1, 66) is wider than the bottom space (refer to FIG. 16). In order to reduce generation of voids in such a portion and maintain a thickness to some extent over the columnar pattern, the film thickness is preferably adjusted to at least a thickness of the narrow pitch portion (in this case, about 200 nm) between the two adjacent patterns each made of the lower semiconductor layer 57, intermediate semiconductor layer 58 and upper semiconductor layer 59. The thickness of this first insulating film is, for example, based on a film existing over the wide pitch portion. It is also possible to form the first insulating film in portions and finally make it totally thick enough to fill the narrow pitch portion.

[0147] As another example, as illustrated in FIG. 22, a row of the columnar laminates (P1, P2) and gate electrode 66 in the Y direction is covered with the first insulating film 70 a as if patterns 172 having a width of about 700 nm and thickness of about 1200 nm are spaced by about 800 to 1000 nm (FIG. 20). The film thickness of the gate electrode 66 is about 40 to 90 nm, while the thickness of the first insulating film over the wide-pitch portion is about 200 to 300 nm.

[0148] As illustrated in FIG. 23, a second insulating film 70 b is deposited over the first insulating film 70 a. Since the underlying layer of this second insulating film 70 b has a line pattern with relatively large width and space, flatness is an important factor for it. When the second insulating film shows a conformal growth, irregularities of the underlying layer (first insulating film 70 a) appears as the irregularities of the second insulating film as is, which will cause troubles in the subsequent steps such as CMP.

[0149] As the second insulating film 70 b, use of an insulating film formed by high-density plasma CVD (which will hereinafter be called “HDP film”) is recommended.

[0150] The high density plasma CVD is a method of forming a film by reacting a raw material gas under the atmosphere of high density (10¹¹/cm² or greater) plasma. Upon reaction, an RF bias is applied to the substrate. In this high density plasma CVD, reaction is accelerated by plasma, while sputter etching due to collision of the plasma with a deposited film occurs. This etching phenomenon occurs preferentially at the protruded portion of the film. When an HDP film is employed as the second insulating film 70 b, its surface is not easily influenced by the irregularities of the underlying layer so that flatness can be secured (FIG. 23).

[0151] Here, an HDP silicon oxide film is employed. It is formed, for example, under conditions of an SiH₄ flow rate of from 70 to 90 sccm, an O₂ flow rate of from 130 to 170 sccm, an argon (Ar) flow rate of from 350 to 450 sccm, and a temperature of from 280 to 400° C. while using silane (SiH₄) and oxygen (O₂) as raw materials. LF is from 3000 to 4000 W, while HF is from 2000 to 3000 W. This generates high density Ar/O₂/SiH₄ plasma.

[0152] Also upon formation of this HDP film, temperature is adjusted to 700° C. or less in order to reduce a thermal stress.

[0153] In order to fill the second insulating film 70 b in a certain depth of the concave portion 170 over the wide pitch portion, it is deposited to a film thickness corresponding to 70% or greater of a vertical difference (H) between the bottom portion of the first insulating film 70 a in the wide pitch portion and the top0 portion existing over the columnar laminates (P1, P2). Here, the thickness of the second insulating film is adjusted to about 600 to 1400 nm. This second insulating film may be formed in portions.

[0154] The vertical difference (H) is almost the height of the columnar laminate (lower semiconductor layer 57, intermediate semiconductor layer 58, upper semiconductor layer 59 and silicon nitride film 62) in FIG. 23. When the plug 55 is formed below the lower semiconductor layer 57, the height of the plug 55 is also included in the vertical difference (refer to FIG. 16).

[0155] Examples of the high-density plasma CVD include electron cyclotron resonance plasma (ECR) CVD, capacitively coupled plasma (IPC) CVD and helicon plasma CVD. For the formation of an HDP film, a manufacturing apparatus for a semiconductor device having, as a plasma source, microwaves, helicon waves, ICP, ECR or the like is used.

[0156] Phosphorous or boron may be doped into the first insulating film (O₃-TEOS film) 70 a to make it a BPSG or PSG film. Fluorine or phosphorous may be doped into the second insulating film (HDP film) 70 b. Thus, gettering effects are available by doping an impurity in an insulating film.

[0157] According to this Embodiment, it is possible to fill the space between columnar patterns with good accuracy, because after the first insulating film having good coverage is deposited with a thickness enough to completely fill the narrow pitch portions, the second insulating film is deposited thereover.

[0158] As illustrated in FIG. 40, when a single layer of the O₃-TEOS film 70 a is formed to a film thickness of about 1 μm in order to fill the wide pitch portions of the columnar patterns (P1, 66) to some extent, a film of about 1 μm thick is inevitably deposited over the columnar patterns owing to excessively good coverage, which cause a marked increase in the surface irregularities. As a result, the flatness over the film cannot be maintained by polishing.

[0159] When the O₃-TEOS film 70 is deposited to a thickness of 1 μm or greater, foreign matters generally tend to appear in a chamber (reaction chamber). The greater the amount of the foreign matters, the higher the frequency of maintenance of the film forming apparatus, leading to a lowering in the productivity. Accordingly, countermeasures against it, for example, formation of an O₃-TEOS film of about 500 nm thick twice is necessary, which makes the manufacturing steps cumbersome.

[0160] A film formation rate of the O₃-TEOS film is slow and it needs about 12 hours for the deposition of a film having a thickness of about 1 μm. Judging from it, filling of the space between the columnar patterns with a single layer of the O₃-TEOS film is very difficult.

[0161] An ordinarily employed HDP film, on the other hand, tends to cause voids when the spacing is 100 nm or less and aspect ratio is 3 or greater. It is accordingly difficult to fill the space between columnar patterns with a single layer of an HDP film.

[0162] Even if the film forming conditions can be adjusted (for example, by increasing a bias power) to improve filling properties, it brings about another problem such as a rise in an etching amount of the exposed gate electrode 66 or silicon nitride film 62 owing to an increase in the sputtering component.

[0163] In addition, the charge-up damage of the exposed gate electrode is increased, leading to a deterioration in device properties.

[0164] In this embodiment, on the other hand, an HDP film used as the second insulating film 70 b. Upon formation of this film, the gate electrode 66 has been covered with the first insulating film 70 a so that etching or charge-up problem of the gate electrode due to a sputtering component can be overcome.

[0165] Filling, with a P-TEOS film 270 d, of the concave portion on the surface of the O₃-TEOS film 70 a as illustrated in FIG. 40 can also be given as one countermeasure (FIG. 41). Also in this case, the surface roughness is large, which may presumably cause an increase in a vertical difference between the memory region (memory cell array) MA and peripheral circuit region PA or a vertical difference between the memory region and a space between a plurality of memory mats MM or memory blocks MB formed in the memory cell array. In the peripheral circuit regions, elements are formed not densely, or over the space between memory mats or memory blocks, almost no pattern but only the O₃-TEOS film and P-TEOS film are formed. In the memory cell array, on the other hand, these films are deposited over the columnar patterns. This causes a vertical difference of about 1 μm.

[0166] On the other hand, the HDP film (70 b) is employed in this embodiment. The film component over the columnar pattern is preferentially etched so that only a thin film is formed over the protruded portion. This makes it possible to reduce a vertical difference between the memory cell array and the peripheral circuit region, or a vertical difference between the memory cell array and a space between a plurality of memory mats formed in the memory array. FIG. 39 is a fragmentary cross-sectional view of the memory cell array (left side) and the peripheral circuit region (right side) after the formation of the HDP film (70 b). In the left side diagram of FIG. 39, layers below the lower semiconductor layer 57 are omitted. In the right side diagram, interconnects or plugs between Qn and Qp, and the first insulating film 70 a are omitted. The Qn and Qp are MISFETs constituting various circuits for driving the memory. The relationship among the peripheral circuit region PA, memory region MA, memory mat MM and memory block MB is shown in FIG. 36.

[0167]FIG. 37 is a fragmentary plan view of the substrate illustrating one example of the layout of the columnar laminate (P) at the boundary of the memory mats MM; and FIG. 38 is a fragmentary plan view of the substrate illustrating one example of the layout of the columnar laminate (P) at the boundary of the memory blocks MB.

[0168] In FIG. 37, the distance between the columnar laminates (P) at the boundary of MM in the X direction is about 1.62 μm, while that in the Y direction is about 1.5 μm.

[0169] In FIG. 38, the distance between the columnar laminates (P) at the boundary of MB in the X direction is about 20 μm.

[0170] The approximately square patterns in these diagrams correspond to a plug 80 which will be described later. Also between MMs or MBs, approximately square patterns (plugs) for, for example, well feed are disposed.

[0171] The distance between any two adjacent MMs or MBs is not limited to the above-described one and they are spaced more narrowly or more widely, depending on the layout.

[0172] What is important here is that use of the HDP film (70 b) makes it possible to maintain flatness of a film over the memory cell array and at the same time, to narrow the above-described vertical difference by depositing a film of a similar thickness over the peripheral circuit region or space between memory mats.

[0173] After formation of a thin O₃-TEOS film, a P-TEOS film may be formed thereover. When the O₃-TEOS film is formed to a thickness as thin as that shown in FIG. 21, however, the concave portion 170 cannot be filled with the P-TEOS film with good accuracy, and slit voids appear in the film. The O₃-TEOS film must be as thick as 600 nm or greater in order to avoid generation of such voids and if so, similar problems which occur when a single layer of the O₃-TEOS film is used for filling.

[0174] According to this Embodiment, on the other hand, the space between columnar patterns can be filled with good accuracy as described above. An insulating film can be filled with good accuracy even if a narrow space portion has an aspect ratio of 3 or greater.

[0175] As illustrated in FIG. 24, after deposition of a P-TEOS film, as the third insulating film 70 c, over the second insulating film 70 b, the surface of the P-TEOS film is polished by CMP to planarize the same.

[0176] As illustrated in FIGS. 25 and 26, the first to third insulating films 70 a to 70 c are etched to withdraw their surfaces, whereby portions of the columnar laminates (P1, P2) on and above a predetermined height are exposed. The term “predetermined height” means a height at which at least the gate electrode 66 over the side walls of the upper semiconductor layer 59 is exposed. In other words, the “predetermined height” is a position between the bottom and the top of the upper semiconductor layer 59.

[0177] Indicated at numeral 172 a in FIG. 26 is a projecting portion of the first insulating film 70 a after this etching and from this projecting portion, a portion and upper portion of the columnar laminates (P1, P2), and the gate electrode 66 over the side walls thereof are protruded.

[0178] The surfaces of the second insulating film and the first insulating film may be withdrawn by etching while carrying out neither deposition of the third insulating film 70 c nor CMP. This step of withdrawing the surface of these insulating films is an important step for controlling the etch back amount of the gate electrode 66 which will be described later. When etching is conducted without reducing the surface irregularities of the insulating film, the surface height tends to vary after etching. Etching after deposition of the third insulating film 70 c and planarization of the surface thereof by CMP therefore facilitates control of the etching amount. In short, it can improve the controllability of etch back of the gate electrode. Or, after deposition of the third insulating film 70 c and CMP are omitted and the surface of the second insulating film 70 b is planarized by CMP, the planarized surface may be etched.

[0179] When the third insulating film 70 c is deposited, some irregularities may appear after the deposition of the second insulating film 70 b, because the third insulating film 70 c relieves the irregularities and CMP planarizes the surface. When the third insulating film is employed, it happens to remain even after this etching.

[0180] An excessively large vertical difference disturbs CMP so that the second insulating film is desirably deposited to give a film thickness of 70% or greater of the vertical difference (H) of the first insulating film 70 a as described above.

[0181] When the third insulating film 70 c is not formed, the thickness of the second insulating film is adjusted so as to completely fill the concave portion 170 over the wide pitch portion. Adjustment of the thickness of the second insulating film 70 b to at least about 1.5 times the vertical difference (H) facilitates flatness control by CMP.

[0182] In the next place, the gate electrode 66 exposed over the side walls of the columnar laminates (P1, P2) is etched so that the upper end portion of the gate electrode will come at the side wall portions of the upper semiconductor layer 59.

[0183] Etching of the gate electrode 66 is conducted in order to expose an upper portion of the upper semiconductor layer 59 which will be a source of the vertical MISFET. The upper end portion of the exposed gate electrode 66 is preferably located over the side wall portions of the upper semiconductor layer 59 in order to prevent a short circuit between the exposed portion (plug 85) and gate electrode 66. An etching amount is controlled so as not to locate the upper end portion of the gate electrode 66 below the upper semiconductor layer 59 in order to prevent offset between the gate electrode 66 and the upper semiconductor layer 59.

[0184] By the steps so far described, formed are p-channel type vertical MISFETs (SV1, SV2) having laminates (P1, P2) each made of the lower semiconductor layer (drain) 57, intermediate semiconductor layer (substrate) 58 and the upper semiconductor layer (source), the gate insulating film 63 formed over the side walls of the laminates (P1, P2) and gate electrode 66.

[0185] As illustrated in FIG. 27, a silicon nitride film is deposited as an insulating film over the second insulating film 70 b by, for example, CVD, followed by anisotropic etching, whereby side wall spacers 71 are formed over the exposed portion of the vertical MISFETs (SV1, SV2), that is, the side walls of the gate electrode 66, the upper semiconductor layer 59 and the silicon nitride film 62 thereover.

[0186] After deposition of a silicon oxide film 73 as a fourth insulating film over the second insulating film 70 b by, for example, CVD, the surface of the silicon oxide film 73 is planarized by CMP. As this fourth insulating film 73, a P-TEOS film, for example, is employed. The fourth insulating film 73 does not necessarily have coverage, because an aspect ratio of the narrowly spaced columnar patterns is reduced by the first and second insulating films. Use of, for example, a P-TEOS film is preferred from the viewpoints of a small thermal stress and a high film forming rate.

[0187]FIG. 28 is a fragmentary cross-sectional view of the substrate after the formation thereover of the silicon oxide film 73. This diagram includes underlying MISFETS (DR1, DR2 and TR1). Indicated at numeral 70 is a laminate of the first insulating film 70 a and the second insulating film 70 b.

[0188] As illustrated in FIGS. 29 and 30, with a photoresist film as a mask, the first, second and fourth insulating films (70 a, 70 b, 73) are dry etched, whereby a through-hole 74 having a bottom extending from the gate extraction electrode 51 a to the intermediate conductive layer 42 and a through-hole 75 having a bottom extending from the gate extraction electrode 51 b to the intermediate conductive layer 43 are formed.

[0189] At the same time, through-holes 76, 77 and 78 from which the surfaces of the intermediate semiconductor layers 41, 44 and 45 are exposed, respectively are formed.

[0190] A Ti film and a TiN film are deposited as a barrier film over the silicon oxide film 73 including the insides of the through-holes 74 to 78 by, for example, sputtering, followed by deposition of a W film as a conductive film by for example, CVD. The W film outside the through-hole is removed by CMP to form a plug 80 inside of the through-holes 74 to 78.

[0191] Via the plug 80 in each of the through-holes 74 and 75, the gate extraction electrodes 51 a and 51 b can be connected to the intermediate conductive layers 42 and 43 (storage nodes A, B) respectively. In other words, the gate electrodes of the two vertical MISFETs can be cross-connected to the storage nodes A and B.

[0192] By the steps so far described, a memory cell having two transfer MISFETs (TR1, TR2), two drive MISFETs (DR1 and DR2) and two vertical MISFETs (SV1, SV2) is substantially completed.

[0193] After deposition of a silicon oxide film 81 as an insulating film over the silicon oxide film 73 by CVD, with a photoresist film as a mask, the silicon oxide films 81, 73 and silicon nitride film 62 over the laminates (P1, P2) are removed by dry etching to expose the upper semiconductor layer (source) 59 of the vertical MISFETs (SV1, SV2), whereby a through-hole 82 is formed.

[0194] The above-described dry etching is conducted as follows: First, when the silicon oxide films 81,73 over the laminates (P1, P2) are removed, etching is terminated temporarily. Since the side wall spacers 71 made of a silicon nitride film are formed over the side walls of the upper semiconductor layer 59, exposure of the gate electrode 66 can be prevented even if a misalignment of the photomask occurs. In the next place, the silicon nitride film 62 is etched.

[0195] Then, the silicon oxide film 81 covering the upper portion of the plug 80 formed in the memory array is etched to form a through-hole 84.

[0196] A TiN film, for example, is deposited as a barrier film over the silicon oxide film 81 including the insides of the through-holes 82,84 by, for example, sputtering, followed by deposition of a W film as a conductive film. The W film outside the through-holes 82,84 are removed by CMP, whereby a plug 85 is formed inside of the through-holes 82,84.

[0197] As illustrated in FIGS. 31 and 32, a silicon carbide film 86 and a silicon oxide film 87 are deposited successively, as an insulating film, over the silicon oxide film 81. With a photoresist film as a mask, the silicon oxide film 87 and silicon carbide film 86 over the through-hole 84 are dry etched to form an interconnect groove 88.

[0198] Over the silicon oxide film 87 including the inside of the interconnect trench 88, a tantalum nitride (TaN) film or a tantalum (Ta) film is deposited as a barrier film by, for example, sputtering, followed by deposition of a copper (Cu) film as a conductive film by sputtering or plating. Then, an unnecessary portion of the Cu film outside the interconnect groove 88 is removed by CMP. These interconnects will become a supply voltage line 90 (Vdd) and complementary data lines (BLT, BLB), and also become an extraction interconnect 92 existing at the end of the memory cell.

[0199] As illustrated in FIGS. 33 and 34, after a three-layer insulating film 93 is deposited over the silicon oxide film 87, an interconnect groove 94 is formed in the insulating film 93. Over the insulating film 93 including the inside of this interconnect groove 94, a Cu film and a TaN film are deposited in the above-described manner, followed by removal of an unnecessary Cu film outside the interconnect groove 94 by CMP. The insulating film 93 is made of, for example, a laminate film of a silicon oxide film, a silicon carbide film and a silicon oxide film deposited by CVD. Upon formation of the interconnect groove 94 in the insulating film 93, an opening 94 a is formed in the interconnect groove 94 over each of the four extraction interconnects 92 formed at the end of the memory cell and a Cu film is formed inside of this opening. These interconnects are to serve as reference voltage line 91 (Vss) and word line (WL).

[0200] In the above-described SRAM memory cell, the columnar laminates constituting the vertical MISFET are formed to have an elliptical pattern, but they may be formed to have an approximately rectangular pattern.

[0201] The underlying MISFETs (DR1, DR2, TR1, TR2) in the SRAM memory cell are able to have various planar layouts.

[0202] As described below, four MISFETs may be used for constituting an SRAM memory cell.

[0203] In this case, drive MISFETS (DR1, DR2) are formed as a relatively lower layer of the memory cell and over the drain region, vertical MISFETs (SV, SV2) are formed. FIG. 42 is an equivalent circuit diagram of a SRAM memory cell in this case. FIGT. 43 is a fragmentary plan view of this memory cell, FIG. 44 is a fragmentary cross-sectional view, in which the left diagram is taken along a line A-A′ of FIG. 43, while the right diagram is taken along a line B-B′ of FIG. 43.

[0204] The drive MISFETS (DR1, DR2) in these diagrams can be formed in a similar manner to that employed in the drive MISFETs illustrated in FIGS. 33 and 34.

[0205] Over the source and drain regions of these MISFETs, plugs (327, 341) are formed in contact holes (324, 340). A reference voltage line 334 is disposed over this plug 327, while vertical MISFETS (SV1, SV2) are disposed over the plug 341 via a connecting conductive layer 346.

[0206] These vertical MISFETS each has a lower semiconductor layer 347, an intermediate semiconductor layer 348, an upper semiconductor layer 349, a gate insulating film 359 formed therearound and a gate electrode 354.

[0207] As illustrated in FIG. 45, there is a difference between a space 3D1, in the X direction, of the vertical MISFETs (SV1, SV2) constituting the memory cell array and a space 3D2 of them in the Y direction. The latter space is greater. These spaces are filled with an insulating film 355 as illustrated in FIG. 44.

[0208] The insulating film is made of a two-layer insulating film, and as illustrated in FIG. 46, the space is filled in two steps by, for example, depositing a first insulating film 355 a and then, a second insulating film 355 b in the space, successively. These insulating films can be formed in a similar manner to the first and second insulating films 70 a,70 b. Of course, a third insulating film may be deposited over the second insulating film 355 b.

[0209] By filling an insulating film in two steps, it is possible to improve the filling property of the insulating film, improve withstand pressure, prevent short circuit and improve properties and yield of the vertical MISFETs.

[0210] In the present memory cell, formation of the first and second insulating films is followed by etching, formation of a word line WL and etch back of the gate electrode 354. Then, a plug (365) and interconnects (BLT, BLB) are formed.

[0211] Indicated at numeral 320 is a silicon nitride film, 321 and 322 silicon oxide films, 328 a silicon nitride film, 329 a silicon oxide film, 331 an interconnect groove, 338 a silicon nitride film, 342 a silicon oxide film, 356 a groove, 357 a polycrystalline silicon film, 358 side wall spacers, 360 a Co silicide layer, 361 a silicon oxide film, 365 a plug, 366 a silicon carbide film, 367 a silicon film and 368 an interconnect groove. Specific manufacturing steps of the SRAM memory cell illustrated in FIG. 44 are described in Japanese Patent Application 2002-199308.

[0212] The memory cell (MC) of FIG. 42 has a structure in which a charge is retained by making use of leak current (I_(OFF) (p)) at the time of OFF of the vertical MISFET (SV1 or SV2) made of a p channel MISFET. The leak current (I_(OFF) (p)) is greater than the leak current (I_(OFF) (n)) of the drive MISFET (DR1 or DR2) which is OFF.

[0213] The inventions made by the present inventors were described specifically based on the above-described embodiments. It should however be borne in mind that the present invention is not limited to or by the above-described embodiments, but can be changed within an extent not departing from the gist of the invention.

[0214] Particularly in the above-described embodiments, the description was made using a SRAM memory cell as an example, but the present invention can be applied widely to semiconductor integrated circuit devices having vertical MISFETs.

[0215] The SRAM memory cell is made of a plurality of MISFETs so that the layout of the vertical MISFETs is limited by the layout of the other MISFETS, which tends to cause a difference between vertical and horizontal pitches of the vertical MISFETs.

[0216] Use of the filling method of the present invention is effective when such a difference appears between the vertical and horizontal pitches of the vertical MISFETs.

[0217] Advantages available by the typical embodiments, out of the embodiments disclosed by the present application, will next be described briefly.

[0218] In the columnar laminates of plural vertical MISFETs which are spaced by a first distance in the first direction and by a second distance, which is greater than the first distance, in the second direction, the first distance portion is filled with a first insulating film and the second distance portion is filled with the first and second insulating films, which makes it possible to improve the filling properties of the insulating films, to improve the properties of the semiconductor integrated circuit device, and to attain miniaturization of the semiconductor integrated circuit device.

[0219] Advantages available by the typical inventions, out of the inventions disclosed by the present application, will next be described briefly.

[0220] Filling properties of a space between the vertical MISFETs constituting the semiconductor integrated circuit device can be improved.

[0221] As another advantage, properties of the semiconductor integrated circuit device can be improved.

[0222] As a further advantage, miniaturization of the semiconductor integrated circuit device can be attained. 

What is claimed is:
 1. A semiconductor integrated circuit device comprising a plurality of vertical MISFETs, wherein the vertical MISFET comprises (a1) a columnar laminate having, at the upper portion and lower portion thereof, a first and second semiconductor regions, respectively, and (a2) a conductive film formed over the side walls of the columnar laminate via a first insulating film, wherein the plurality of vertical MISFETs having the columnar laminate and the conductive film are (b1) spaced by a first distance in a first direction, and (b2) spaced by a second distance, which is greater than the first distance, in a second direction, and wherein up to at least a predetermined height of the columnar laminate of the plurality of vertical MISFETs, (c1) a second insulating film is formed in a space between the columnar laminates in the first direction, and (c2) the second insulating film and a third insulating film lying thereover are formed in a space between the columnar laminates in the second direction.
 2. A semiconductor integrated circuit device, comprising: a plurality of vertical MISFETs each including, (a1) a columnar laminate having, at the upper portion and lower portion thereof, first and second semiconductor regions respectively, and (a2) a conductive film formed over the side walls of the columnar laminate via a first insulating film, wherein said vertical MISFETs is arranged in an array form, such that (b1) the vertical MISFETs are spaced by a first distance in a first direction, and such that (b2) vertical MISFETs are spaced by a second distance, which is greater than the first distance, in a second direction; (c) a second insulating film having, embedded therein, the vertical MISFETs aligned in the first direction, out of the plurality of vertical MISFETs, and having a plurality of projecting portions extending in the first direction; and (d) a third insulating film formed between the plurality of projecting portions of the second insulating film.
 3. A semiconductor integrated circuit device according to claim 1, wherein the second insulating film has better coverage than the third insulating film.
 4. A semiconductor integrated circuit device according to claim 1, wherein the second insulating film is a silicon oxide film formed by chemical vapor deposition by using tetraethoxysilane as a raw material, and the third insulating film is a silicon oxide film formed under a plasma atmosphere having a plasma density of 10¹¹/cm² or greater.
 5. A semiconductor integrated circuit device according to claim 4, wherein the second insulating film is a silicon oxide film formed by chemical vapor deposition by using tetraethoxysilane and ozone (O₃) as raw materials.
 6. A semiconductor integrated circuit device according to claim 1, wherein the columnar laminate has a high at least 3 times as much as that of the first distance.
 7. A semiconductor integrated circuit device according to claim 1, wherein the first distance is 150 nm or less, while the second distance is 500 nm or greater.
 8. A semiconductor integrated circuit device according to claim 1, wherein a fourth insulating film is filled in spaces, in the first direction and in the second direction, between the columnar laminates on and above a predetermined height thereof.
 9. A semiconductor integrated circuit device according to claim 1, wherein a thickness of the second insulating film in the space between the columnar laminates in the second direction is the first distance or greater.
 10. A semiconductor integrated circuit device according to claim 1, wherein the plane pattern of the columnar laminate and the conductive film over the side walls thereof is approximately elliptical and a first diameter in the first direction is smaller than a second diameter in the second direction.
 11. A semiconductor integrated circuit device according to claim 1, wherein the predetermined height exists between the bottom and top of the first semiconductor region.
 12. A semiconductor integrated circuit device according to claim 1, wherein the plurality of vertical MISFETs constitute a plurality of memory cells disposed in the array form in the first and second directions, the memory cells each including: (d1) of the plurality of vertical MISFETs, two vertical MISFETs adjacent in the first direction; (d2) two horizontal drive MISFETs connected to the respective second semiconductor regions of the two vertical MISFETs, respectively, and together with the two vertical MISFETs, constituting a pair of inverters having input and output portions cross-connected; and (d3) two horizontal transfer MISFETs each connected between the second semiconductor region of each of the two vertical MISFETs and a first line pair and having a gate electrode connected to a second line, (d4) wherein the two horizontal drive MISFETs and two horizontal transfer MISFETs are formed below the second semiconductor region.
 13. A semiconductor integrated circuit device according to claim 1, wherein the plurality of vertical MISFETs constitute a plurality of memory cells disposed in the array form in the first and second directions, the memory cells each including: (d1) of the plurality of vertical MISFETs, two vertical MISFETs which are adjacent in the first direction, in which each has the second semiconductor region connected to a first line pair, and each has the conductive film connected to a second line; (d2) two horizontal drive MISFETs connected between each of the second semiconductor regions of the two vertical MISFETs and a reference potential, and having a gate electrode cross-connected to each of the second semiconductor regions of the two vertical MISFETs, (d3) wherein the two horizontal drive MISFETs are formed below the second semiconductor region.
 14. A semiconductor integrated circuit device according to claim 12, wherein a single region in which the memory cell is formed is approximately rectangular and the length thereof is greater in the second direction than that in the first direction.
 15. A manufacturing method of a semiconductor integrated circuit device, comprising the steps of: (a) forming a plurality of columnar laminates having, at the upper portion and lower portions thereof, a first semiconductor region and a second semiconductor region, respectively, while spacing the plurality of columnar laminates in a first direction and in a second direction wider than the first direction; (b) forming conductive films over the side walls of the columnar laminates via a first insulating film with a distance, in the first direction, between the conductive films over the side walls of the plurality of columnar laminates as a first distance and with a distance in the second direction as a second distance which is greater than the first distance; (c) forming a second insulating film to a thickness enough to fill a space of the first distance and but not enough to fill a space of the second distance; and (d) forming a third insulating film over the second insulating film and filling the space of the second distance.
 16. A manufacturing method of a semiconductor integrated circuit device, comprising the steps of: (a) forming a plurality of columnar laminates having, at the upper portion and lower portions thereof, a first semiconductor region and a second semiconductor region, respectively, while spacing the plurality of columnar laminates in a first direction and in a second direction wider than the first direction; (b) forming conductive films over the side walls of the columnar laminates via a first insulating film with a distance, in the first direction, between the conductive films over the side walls of the plurality of columnar laminates as a first distance and with a distance in the second direction as a second distance which is greater than the first distance; (c) depositing a second insulating film between the columnar laminates and thereover with a thickness at least equal to the first distance; and (d) depositing over the second insulating film a third insulating film with a thickness corresponding to at least 70% of a vertical difference, after the step (c), between the top of the second insulating film over the second distance portion of the columnar laminates and the top of the second insulating film over the columnar laminates.
 17. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the step (c) is carried out at a temperature of 700° C. or less.
 18. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the step (c) and the step (d) are carried out at a temperature of 700° C. or less.
 19. A manufacturing method of a semiconductor integrated circuit device according to claim 15, further comprising, after the step (d), the steps of: (e) depositing a fourth insulating film over the third insulating film; and (f) etching the second, third and fourth insulating films until the conductive film existing over the side walls of the first semiconductor region of the columnar laminate is exposed.
 20. A manufacturing method of a semiconductor integrated circuit device according to claim 19, further comprising, after the step (g), a steps of: (h) forming a fifth insulating film over the second and third insulating films.
 21. A manufacturing method of a semiconductor integrated circuit device according to claim 15, further comprising, after the step (d), the steps of: (e) etching the second and third insulating films until the conductive film existing over the side walls of the first semiconductor region of the columnar laminate is exposed; and (f) etching the conductive film exposed by the step (e).
 22. A manufacturing method of a semiconductor integrated circuit device according to claim 21, further comprising, after the step (f), a step of: (g) forming a fourth insulating film over the second and third insulating films.
 23. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the second insulating film has better coverage than the third insulating film.
 24. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the second insulating film is a silicon oxide film and the step (c) is carried out by chemical vapor deposition using tetraethoxysilane as a raw material.
 25. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the second insulating film is a silicon oxide film and the step (c) is carried out by chemical vapor deposition using tetraethoxysilane and ozone (O₃) as raw materials.
 26. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the third insulating film is a silicon oxide film and the step (d) is carried out in a plasma atmosphere having a plasma density of 10¹¹/cm² or greater.
 27. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the columnar laminate has a height of at least 3 times as much as the first distance.
 28. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the first distance is 150 nm or less and the second distance is 500 nm or greater.
 29. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the plane pattern of each of the columnar laminate and the conductive film over the side walls thereof is approximately elliptical and a first diameter in the first direction is smaller than a second diameter in the second direction.
 30. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the columnar laminate in the step (a) is formed using a mask which is H-shaped in the first direction.
 31. A manufacturing method of a semiconductor integrated circuit device according to claim 15, further comprising, prior to the step (a), the steps of: (h) forming two pairs of horizontal MISFETs having source and drain regions in common; and (i) connecting the second semiconductor regions of the two vertical MISFETs adjacent to each other in the first direction to the source and drain regions which the two pairs of horizontal MISFETs have in common, respectively.
 32. A manufacturing method of a semiconductor integrated circuit device according to claim 15, further comprising, prior to the step (a), the steps of: (j) forming two horizontal MISFETs; and (k) connecting the second semiconductor regions of the two vertical MISFETs adjacent to each other in the first direction to one ends of the two horizontal MISFETs, respectively.
 33. A manufacturing method of a semiconductor integrated circuit device, comprising the steps of: (a) forming a semiconductor film having, at the upper and lower portions thereof, first and second semiconductor regions, respectively; (b) etching the semiconductor film through a mask which is H-shaped in first direction, thereby forming an approximately elliptical columnar laminate having a longer diameter in a second direction perpendicular to the first direction; and (c) forming a conductive film over the side walls of the approximately elliptical columnar laminate via an insulating film.
 34. A manufacturing method of a semiconductor integrated circuit device comprising a plurality of vertical MISFETs, wherein the vertical MISFET comprises (a1) a columnar laminate having, at the upper and lower portions thereof, first and second semiconductor regions, respectively, and (a2) a conductive film formed over the side walls of the columnar laminate via a first insulating film, wherein said plurality of vertical MISFETs having the columnar laminate and conductive film are (b1) spaced by a first distance in a first direction, and (b2) spaced by a second distance, which is greater than the first distance, in a second direction, (c) the plane pattern of the columnar laminate and the conductive film over the side walls thereof being approximately elliptical, and a first diameter in the first direction being smaller than a second diameter in the second direction, the method comprising the steps of: (d) forming a semiconductor film, having at the upper and lower portions thereof, first and second semiconductor regions, respectively; and (e) etching the semiconductor film via a mask which is H-shaped in the first direction, thereby forming an approximately elliptical columnar laminate having a longer diameter in a second direction perpendicular to the first direction.
 35. A manufacturing method of a semiconductor integrated circuit device according to claim 33, wherein the steps are for the formation of vertical MISFETs constituting a SRAM, and a single memory cell formation region of the SRAM is approximately rectangular with a long side in the second direction.
 36. A semiconductor integrated circuit device according to claim 33, wherein the H-shaped mask is a transfer mask used in photolithography, an approximately elliptical columnar pattern for etching is formed using the H-shaped transfer mask, and the semiconductor film is processed into an approximately elliptical columnar laminate by using the etching pattern.
 37. A semiconductor integrated circuit device according to claim 36, wherein the H-shaped mask has a structure in which the width of the mask in the first direction is narrower at the center of the mask in the second direction than at the both ends.
 38. A semiconductor integrated circuit device, comprising: (a) a columnar laminate having, at the upper and lower portions thereof, first and second semiconductor regions, respectively and having an approximately elliptical plane pattern; and (b) a conductive film formed over the side walls of the columnar laminate via an insulating film.
 39. A semiconductor integrated circuit device comprising a plurality of vertical MISFETs including: (a1) a columnar laminate having, at the upper portion and lower portion thereof, first and second semiconductor regions, respectively; and (a2) a conductive film formed over side walls of the columnar laminate via a first insulating film, wherein the plurality of vertical MISFETs having the columnar laminate and the conductive film are (b1) spaced by a first distance in a first direction, and (b2) spaced by a second distance, which is greater than the first distance, in a second direction, and (c) wherein a plane pattern of the columnar laminate and the conductive film over the side walls thereof is approximately elliptical and a first diameter in the first direction is smaller than a second diameter in the second direction.
 40. A semiconductor integrated circuit device according to claim 38, wherein the columnar laminate constitutes the vertical MISFET of SRAM, and a single memory cell formation region of the SRAM is approximately rectangular and has a long side in the direction of a longer diameter of the approximately elliptical shape.
 41. A semiconductor integrated circuit device according to claim 1, wherein the conductive film is formed to encompass the columnar laminate.
 42. A manufacturing method of a semiconductor integrated circuit device according to claim 15, wherein the conductive film is formed to encompass the columnar laminate. 